HANTEX A-160

complete substitution of PTF

A-160 is a high quality paint thickener, high concentration of the thickener, water and a dispersion stabilizer Chi, fast and thickened lubricating coating designed for textile printing process.

Chemical Composition:

acrylic polymer dispersion

Nature:

• Ionic: anionic
• Physical Form: White pourable dispersion
• pH of the system (by non-1%): Approximately 6.0
• towers Volume: > 60%
• Viscosity(CPS): <3000cps
• gravity: 1.05~ 1.10

Features:

Excellent color yield and vividness, printing effect, duck outline clear, impermeability of high thickening effect, can quickly adjust the rheology and viscosity of the printing paste, printing paste can be added directly to the soft, very easy to use, does not contain a wake, non-APEO, comply with Oeko-Tex l00

Application:

Reserve pulp preparation before adding water, high genetic mixing, slowly add paint thickener PTF, stir into a smooth, no lumps of paste. Another time a large number of high shear mixing will heat may result in decreased viscosity.

• Water: 98.2kg
• A-160: 1.8kg
• Total: 100 kg

Direct added:

As the paint thickener PTF has excellent hydrating properties, increasing towers quickly, so can be "directly into the Law" to adjust the slurry viscosity requirements depending on the machine, the proposed amount of about 1.5-2% Chi.

Storage:

A-160 should be stored in the original containers, or other glass, stainless steel, plastic or container with epoxy in the village.

Packing:

plastic bucket packaging 50/125kg

HANTEX RBT-280

Sodium alginate substitutu, complete substitution of algin

Uses:

HANTEX RBT-280 is suitable for cotton and synthetic activity, disperse dyes printing synthetic thickener.

Composition:

Chemical composition: acrylic polymer dispersion

Nature:

• Ionic: anionic
• Physical Form: White pourable dispersion
• pH of the system (by non-1%): Approximately 6.0

Stability:

neutral to alkaline stability and resistance to hard water may precipitate in strong acid.

Features:

Good rheological - compared with the conventional thickeners can achieve higher color yield, better clarity and smoothness. Thickening fast, stable - reducing reserves slurry preparation time, the pulp is not caking. Good resistance to electrolyte stability - stability while maintaining good viscosity increases towers reserve pulp. Depending on the production process requires appropriate changes.

Application:

HANTEX RBT-280 suitable for one-phase or two-phase type, and all the printing process, fixing method, active thickener PAD or sodium alginate may be combined with the use of kerosene, the use of stirring while adding the mixture was stirred until dissolved uniformly to available.

Average printing viscosity:

• Flat Screen: 15,000~30,000cPs (55~70g/kg active agent increases towers HANTEX RBT-280)
• Roller: 6,000~15,000 cPs (40~60g/kg HANTEX RBT-280)

Compared with the sodium alginate, when using active thickener 5g/kg HANTEX RBT-280 must add sodium carbonate. Usually bases are suitable for the activity of the HANTEX RBT-280, such as sodium carbonate, sodium bicarbonate, potassium carbonate. Restricted by the dye, the storage stability of sodium bicarbonate to give the longest paste. When using sodium bicarbonate to ensure that the lowest concentration of 25g/kg.

Curtain recommended dosage for reference only. Taking into account more types of fabrics and dye compounds, the proposed preliminary experiments. Attached to the surface of fabric dyes and chemicals must be removed by a standard washing procedure, the most important is first softened in cold water swelling thickening agent can account for easy removal.

Storage:

seal can be stored for 12 months in the dark place

Packing:

plastic bucket packaging 50/125kg